What is 1100 h14 aluminum?
This alloy is commercially pure aluminum with a minimum of 99.00% purity. It has high thermal conductivity with excellent corrosion resistance, workability and weldability. Deep drawn applications, spinning, fan blades, nameplates and metal work are typical applications.
What is 1100 series aluminum?
1100 aluminium alloy is an aluminium-based alloy in the “commercially pure” wrought family (1000 or 1xxx series). With a minimum of 99.0% aluminium, it is the most heavily alloyed of the 1000 series. It is also the mechanically strongest alloy in the series, and is the only 1000-series alloy commonly used in rivets.
How strong is 1100 aluminum?
Aluminum 1100
| Properties | Metric | English |
|---|---|---|
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi |
| Elongation at Break | 15 – 28% | 15 – 28% |
| Modulus of Elasticity | 68.9 GPa | 103000 ksi |
What is the density of pure aluminum?
The density of aluminium is about 2,710kg/m3. The density of the alloys of aluminium does not vary widely from this figure ranging between 2,640kg/m3 and 2,810kg/m3.
What are the different types of aluminum?
Different Aluminum Grades Aluminum comes in three basic types: 1100, 3003, and 6061. The grade of the aluminum will determine the end-use application and price point. For example, 1100 is a lower-cost material than 6061 but cannot be used for high-temperature applications like cooking utensils or pot lids.
What is 1100 Aluminium alloy used for?
Applications. Aluminium / Aluminum 1100 alloy is widely used in fin stock, heat exchanger fins, spun hollowware, dials and name plates, decorative parts, giftware, cooking utensils, rivets and reflectors, and in sheet metal work.
Can you heat treat 1100 aluminum?
Aluminum 1100 is just one of several common aluminum alloys and is soft, low strength and, at 99% min aluminum, is the commercially pure aluminum. Copper, iron, magnesium, manganese, silicon, titanium, vanadium and zinc comprise the remaining elements. It cannot be hardened by heat treatment and is very formable.
What is the hardest grade of aluminum?
Known as the zinc grades – zinc being the largest alloying element, the 7000 series grades are the hardest and strongest commercial grades of aluminium. Grade 7075 is the most common of the 7000 series grades. It is an extremely high strength alloy; the strongest of all commercial grades of aluminium.
What is 1100 aluminum?
Aluminum 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance.
What is 1100 alloy?
1100 aluminium alloy is an aluminium-based alloy in the “commercially pure” wrought family (1000 or 1xxx series). With a minimum of 99.0% aluminum, it is the most heavily alloyed of the 1000 series. It is also the mechanically strongest alloy in the series, and is the only 1000-series alloy commonly used in rivets.
What is Al 1100?
Foil, Sheet, Bar & Plate All Tempers. It work-hardens slowly, and is not heat-treatable. It has excellent corrosion resistance and weldability, and is most often used in the food processing and chemical industries . Al 1100 is noted for having the highest thermal conductivity of any aluminum, and is also known for its high electrical conductivity.
What is the density of aluminum alloy?
DENSITY OF ALUMINUM. The density of aluminum is about 0.1 lb/in3 [2,700 kg/m3] and density values of aluminum alloys don’t vary much. Aluminum and aluminum alloys are characterized by a relatively low density compared to steel.