What is the shear strength of 316 stainless steel?
For 316 stainless, the tensile strength is about 84,000 psi, so the shear strength is roughly 50,000 psi.
Is 316 stainless steel ductile or brittle?
The types of stainless steels present is quite high and they range from very ductile malleable, deformable austenitic (FCC) nickel and chromium rich steels, like the AISI 316 to strong, brittle, martensitic, precipitation hardened steels like the 17-7PH.
What is meant by yield strength?
Yield strength refers to an indication of maximum stress that can be developed in a material without causing plastic deformation. It is the stress at which a material exhibits a specified permanent deformation and is a practical approximation of the elastic limit.
What is the density of 316 stainless steel?
7.99 g/cm3
Physical Properties (Room Temperature)
| Specific Heat (0-100°C) | 500 | J.kg-1.°K-1 |
|---|---|---|
| Thermal Expansion | 15.9 | μm/μm/°C |
| Modulus Elasticity | 193 | GPa |
| Electrical Resistivity | 7.4 | μohm/cm |
| Density | 7.99 | g/cm3 |
What is the Brinell hardness of 316 stainless steel?
Annealed 316 stainless steel has a Brinell scale hardness of 149, and Rockwell hardness of B80.
What is the melting point of 316 stainless steel?
As stated in an AK Steel data sheet for grade 316 stainless steel, the melting range of 316 SS is 2,500 °F – 2,550 °F (1,371 °C – 1,399 °C), roughly 50 to 100 degrees Fahrenheit lower than the melting point of grade 304 stainless.
What is the allowable stress for stainless steel?
For austenitic stainless steel pipe ASTM A312 TP316 pipe, the allowable stress is (1/3) of tensile strength up to temperature of 300°F as discussed in above section. As the temperature exceeds 300°F and up to 1050°F, the allowable stress will be lower of (2/3) of yield strength at room temperature and 90% of yield strength at the applicable temperature.
What is the tensile strength of AISI 316 stainless steel?
AISI Type 316 Stainless Steel, annealed bar Physical Properties Metric Comments Hardness, Rockwell B 80 Hardness, Vickers 155 Converted from Brinell hardness. Tensile Strength, Ultimate 550 MPa Tensile Strength, Yield 240 MPa